Thermal Spraying
Fe-Basis
Title | Composition | ||||||||||||
Cr % |
Ni % |
Si % |
B % |
Mo % |
Nb % |
Al % |
W % |
Mn |
C | other | hardness | Features / Application | |
SP 100 | 17 | 0,1 | 30-35 HRC |
Repair of machinery components | |||||||||
SP 101 | 22 | 0,5 | 4,5 | 4,0 | 3,5 | 6,5 | 1,2 | 68 - 70 HRc |
Friction metal-metal, screws, mixers, hot sieves | ||||
SP 102 | 20 | 1,5 | 1,5 | 1,0 | 0,6 | 3,5 Ti | 850 HV 0,3 | Abrasion-and erosion-resistant to 650 °C, high bonding strength | |||||
SP 103 | 25 | 10 | 1,2 | 2 | 4 | 1,2 | 0,5 | 2 Cu | 45 HRc | Polishable, good wear resistance at temperatures up to 870 °C, repair coating | |||
SP 104 | 21 | 8 | 1,1 | 2,3 | 3,2 | 1,2 | 0,2 | 2 Cu | 53 HRc | Self compacting up to 1000 HV, good grinding, high elasticity, used as bond and top coat | |||
SP 105 HY | 20 | 2,8 | 11 | 0,25 | 11 Co | 350 HB | Cavitation-resistant, resistant to erosion, water turbine, hydraulic | ||||||
SP 106 | 14 | 4,5 | 1,3 | 1,9 | 26 | 0,6 | 6 TIC | 66 HRc | Very good abrasion resistance, anti-slip surfaces in industrial walkways and deck | ||||
SP 107 | 19 | 8,5 | 0,4 | 6 | 0,1 | 400 HB | Good corrosion resistance, hardening, good machinability, repair coating | ||||||
SP 108 | 26 | 3 | 1,6 | 0,8 | 1,6 | 1,7 | 40-42 HRc | Resistant to abrasion, corrosion, good to machine | |||||
SP 111 | 30 | 1,3 | 2,8 | 1,0 | 40-45 HRc | Low coeffi cient of friction, chrome replacement coatings, valve stem, plunger, shaft, bearing seats | |||||||
SP 112 | 27,5 | 1,5 | 3,8 | 1,5 | 0,1 | 1000-1150 HV 0,1 | Boiler erosion protection, temperature up to 650 °C | ||||||
SP 113 | 18 | 12 | 0,8 | 2,7 | 1,7 | 0,12 | 200-240 HV | Comparable to 316L, good corrosion resistance | |||||
SP 118Y | 22 | 5 | 1 Y | 170-270 HV 0,3 | Good corrosion protection in gas atmosphere to Sulfur and Carbon, temperature resistant up to 500 °C, good mechanical machinability, boiler tubes |
Corodur Fülldraht GmbH may change the characteristics of the wire without notice. Statements on composition and application are just for the applier's information. Statements on mechanical properties always refer to the all-weld-metal according to valid standards. We recommend the applier to check our products for their special application autonomously.
Ni-Basis
Title | Composition | ||||||||||
Cr % |
Si % |
B % |
W % |
Mo % |
Nb % |
C % |
Al % |
other |
Hardness | Features/ Application | |
SP 201 | 20 | 4,7 | 3,2 | 0,7 | 500-800 HV 0,1 | Self-fluxing alloy, can be sintered components for chemical plants, food industry, plunger |
|||||
SP 206 | 20 | 4,5 | 1,6 | 2 | 0,35 | 500-800 HV 0,1 | Self-fluxing alloy, can be sintered components for chemical plants, food industry, plunger | ||||
SP 212 | 20 | 4,9 | 2,8 | 2,5 | 0,6 | 5 Fe | |||||
SP 221 | 20 | 4,5 | 0,7 | 2 | 0,4 | 500-800 HV 0,1 | Boiler wood class A1+A2 | ||||
SP 222 | 20 | 90 HRB | Bond coat in aggressive environment | ||||||||
SP 223 | 50 | 250-280 HV | Good resistance against Sulfur up to temperatures of 650°C, coal fired power plants, black liquor boiler | ||||||||
SP 224 | 45 | 1 Ti | 32 HRc | Good resistance in boiler environment under presence of S, V up to temperatures of 650°C, coal fired power plants, tubes, water walls | |||||||
SP 225 | 22 | 9 | 3,5 | 0,05 | 240-300 HV 0,1 | High corrosion resistant against acids with Chlorines, resistant against oxidation and hot gas corrosion as bond coat and for repair chemical industry |
|||||
SP 226 | 16 | 5 | 17 | 0,1 | 200-240 HB | High acid restance under presence of Chlorides, resistant against oxidation and hot gas corrosion chemical industry, petro chemical industry, off shore applications |
|||||
SP 227 | 15 | 3,5 | 1,5 | 0,1 | 35 HRc | High acid restance under presence of Chlorides, resistant against oxidation and hot gas corrosion chemical industry, petro chemical industry, off shore applications |
|||||
SP 228 | 25 | 0,4 | 2 | 0,4 | 15 SC | 700-1000 HV 0,1 | Hard face coating |
||||
SP 229 | 20 | 55-80 HRB | Dense coatings with increased oxidation resistance and HT corrosion resistance up to 650°C, self bonding bond coat |
||||||||
SP 230 | 5 | 65 HRB | Bond coat | ||||||||
SP 231 | 6 | 5 | 78 HRB | Exceptional high bond strength due to exothermic reaction for bond coats for repair of machinable C-steels and corrosion resistant steels increased wear resistance through Mo repairs, bearings, good particle erosion resistance | |||||||
SP 232 | 8 | 5 | 7 | 5 Fe | 100-120 | For repair coating, good machnability corrosion resistant |
Corodur Fülldraht GmbH may change the characteristics of the wire without notice. Statements on composition and application are just for the applier's information. Statements on mechanical properties always refer to the all-weld-metal according to valid standards. We recommend the applier to check our products for their special application autonomously.