CORODUR® 69

CLASSIFICATION

DIN EN 14700 | DIN 8555
T Fe16 | MF 10-65-GRZ

GENERAL CHARACTERISTICS

CORODUR 69 is a tubular wire for extreme abrasive wear, even at high temperatures up to 650°C. The deposit has a very fine ledeburitic structure, bearing a lot of different very hard carbides. CORODUR 69 is used, wherever abrasive wear is extremely high. It is also wear resistant at high temperatures up to 650 °C. Due to the high hardness pre heating of the base metal is recommended. The deposit should be subjected to little impact stress. The deposit is nearly free of slag; the weldability is excellent. Good results are already achieved by welding one layer. A maximum deposit thickness of 6 to 8 mm (2 layers) is recommended. The resulting deposits cannot be heattreated, machined or forged. Before overlaying on old previously hard-faced surfaces a buffering layer of CORODUR 200 K or 250 K is recommended.

APPLICATION

Concrete-industry, mixer parts, extruder, scrapers, sintering grates, mining

TYPICAL ALL WELD METAL ANALYSIS (%)

C Si Mn Cr Nb B
5,2 0,8 0,4 32,5 5,8 1,8

TYPICAL ALL WELD METAL MECHANICAL PROPERTIES

Hardness: 64 – 67 HRc

PARAMETER

Diameter Voltage Amps
1,6 20-26 160-260
2,0 22-26 240-280
2,4 24-27 280-340
2,8 25-28 320-400

FORMS OF DELIVERY

Coil "BS 300" = 15 kg Coil "BS 450" = 25 kg Drums = 300 kg

OA = gasless


Corodur Fülldraht GmbH may change the characteristics of the wire without notice. Statements on composition and application are just for the applier’s information. Statements on mechanical properties always refer to the all-weld-metal according to valid standards. We recommend the applier to check our products for their special application autonomously.