COROCARB FE
CLASSIFICATION
DIN EN 14700 | DIN 8555
T Fe20 | MF 21-65-GZ
GENERAL CHARACTERISTICS
COROCARB OA is an open arc tubular wire filled with fused tungsten carbide (FTC) for semi-automatic application, where extreme abrasive wear is encountered. For hardfacing of low alloyed steels that have a maximum of 0,45% carbon (a higher carbon content could lead to cracking). Also for hardfacing and repairing tools and machine parts exposed to wear. The area to be hardfaced should be free of rust, scale, grease or other dirt. Depending on the base metal’s alloy and the size of the area to be hardfaced the advisable preheating temperature should be between 350-500°C (662-932°F). If the voltage and the welding current are kept on the lowest setting possible the tungsten carbide granular will be prevented from melting. During welding, position the arc that the weld metal is deposited in coarse droplets.
APPLICATION
Mining, excavation, earth moving, tunneling shields, road construction, well drilling and deep drilling.
TYPICAL ALL WELD METAL ANALYSIS (%):
Fe- C- Co- W – Matrix + 62% WSC (2400 HV0,2)
TYPICAL ALL WELD METAL MECHANICAL PROPERTIES
WELD METAL:
1st layer approx. 60 - 62 HRC
2nd layer approx. 62 - 66 HRC
FTC: approx. 2400 HV0,2
PARAMETER
| Diameter | Voltage | Amps |
| 1,2 | 22 - 26 | 140 - 180 |
| 1,6 | 22 - 26 | 180 - 240 |
| 2,0 | 25 - 27 | 220 - 260 |
| 2,4 | 25 - 27 | 260 - 300 |
| 2,8 | 26 - 28 | 280 - 340 |
FORMS OF DELIVERY
| Coil "BS 300" = 15 kg | Coil "BS 450" = 25 kg | Drums = 300 kg |
OA = gasless, G = gas shielded
Corodur Fülldraht GmbH may change the characteristics of the wire without notice. Statements on composition and application are just for the applier’s information. Statements on mechanical properties always refer to the all-weld-metal according to valid standards. We recommend the applier to check our products for their special application autonomously.